Highly resistant facade paint EXTERLIT LOZANGE

190.5 USD

Special conditions

Supplier: Lacos

Description

High quality matte microporous paint based on Pliolite resinin a solution of white spirit with high performance properties. Designed to upgrade new and old facades. Is used at the exterior facades, even alkaline surfaces concrete, asbestos cement, brick, stucco. Has excellent adhesion to surfaces previously painted with vinyl or silicate paint — Has a high resistance to weathering in extreme conditions in a humid, Maritime climate and the far North, when operating on the plinths of buildings — Forms a microporous film, which allows the base to breathe and at the same time to provide them water resistant — Good on all surfaces even alkaline — Frost-resistant, can be applied at low temperatures (to minus 20°C), provided that the substrate is not frozen — Has excellent coverage With low odor — Does not require priming the surface Durability at least 25 years Certificate of conformity № ROSS RU.АЮ31.Н12735 from 25.05.2011 G. The certificate of state registration № RU.77.01.34.015.E.022075.12.11 from 23.12.2011 Exterior paint EXTERLITH LOSANGE included in the list of certified coatings recommended in Passports "Color palette, materials and the technology of the works" for objects of Moscow. Paint EXTERLITH LOSANGE gold medal at the international exhibition "INTERLAKOKRASKA".

Characteristics

conditional lightfastness,%: 2.9 (GOST 21903-96)
packing: 1 l; 4 l; 15 l
safety engineering: flammable, keep away from fire, store in a tightly closed container
shelf life: 5 years from the date of manufacture in original packaging at a temperature of plus (5-30) С
appearance: thick paint, slightly thixotropic
water resistance: 2 hours after application, the coating is resistant to water
covering rate of the dried film, g / m2: 120 - 150 (GOST 8784-75)
resistance to vapor permeation, m2hPa / mg: no more than 0.15 (GOST 25898-83)
Colour: all colors of the DECOCOLOR, RAL-5K, NCS-2 and NUANCIER FACADE catalogs
film adhesion to concrete, MPa: 2.25 (GOST 28574-90)
film-to-metal adhesion, point: 1 (GOST 15140-78, method 2)
стойкость пленки к статическому воздействию: - воды при 20 °С, ч - 5 %-ного раствора NaOH при 20 °С, ч: 24 (GOST 9.403-80, method A) 24 (GOST 9.403-80, method A)
vapor permeability coefficient, mg / mhPa: not less than 0.02 (GOST 28575-90)
resistance of the coating to climatic factors, cycles: 100 (GOST 9.401-91, method 2U.1)
film adhesion after climatic tests, MPa: 1.24 (GOST 28574-90)
diluent: white spirit, VARSOL D40 brand recommended
density at 23 ° С: 1.52 - 1.62 g / cm3
type of dry layer: matt
consumption: 0.10 - 0.15 l / m2 per layer
drying time: at (202) ° С and relative air humidity (655)% of dust adhesion - 2 hours, reapplication after 12 hours
base: P (pastel tones), M (semi-saturated tones), Tr (saturated tones)
durability: at least 10 years depending on the type of substrate, environmental conditions and if the requirements for surface preparation, application and maintenance of the coating are observed